Bostrand 316LSi

The following items have been added to your list


x

A continuous solid corrosion resisting chroumium-nickel-molybdenium wire for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo types. Bostrand 316LSi has a good general corrosion resistance, in particularly the alloy has very good resistance against corrosion in acid and chlorinated environments. The alloy has a low carbon content which makes it particularly recommended where there is a risc of intergranular corrosion. The higher silicon content improves the welding properties, such as wetting. The alloy is widely used in the chemical and food processing industries as well as in ship building and various types of architectural structures.

BUY NOW


Typical Charpy V-Notch Properties

as welded

Typical Tensile Properties

Condition As Welded As Welded
Shielding Gas Tested at 350°C.
Tensile Strength 560 MPa (81 ksi) 440 MPa (64 ksi)
Yield Strength 400 MPa (58 ksi) 340 MPa (49 ksi)
Elongation 37 % 26 %

Deposition Data

Current Deposition Rate Diameter Voltage Wire Feed Speed
55-160 A 1.0-4.1 kg/h (2.2-9.0 lb/h) 0.8 mm (0.030 in.) 12-24 V 4.0-17.0 m/min (157-669 in./min)
80-240 A 1.5-6.0 kg/h (3.3-13. lb/h) 1.0 mm (0.040 in.) 15-28 V 4.0-16.0 m/min (157-630 in./min)
100-300 A 1.6-7.5 kg/h (3.5-16. lb/h) 1.2 mm (0.047 in.) 15-29 V 3.0-14.0 m/min (118-551 in./min)

Classifications

Wire Electrode EN ISO 14343 : G 19 12 3 LSi
SFA/AWS A5.9 : ER316LSi
Werkstoffnummer : ~1.4430

Consumable Characteristics

Alloy Type Austenitic (with 8%ferrite)
Shielding Gas M12, M13 (ISO 14175)

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C Cr Cu Mn Mo Ni P S Si
0.02 % 18.5 % 0.1 % 1.8 % 2.7 % 12 % 0.015 % 0.015 % 0.8 %